Technical Data Base: 1 C.-Polyoxypropylener Density: 1,44 g/cm³ Viscosity Adhesive: Pasty Stability/Run-off (ASTM D 222): 1 mm Processing Temperature: +5 to +40 °C Cure Type: By Humidity Curing Condition: +5 to +40°C and 30% to 95% rel. humidity Skin-Overtime*: 25 min.

Curing Speed ( first 24h): 2 -3 mm Volume Change (DIN 52451): -1 % Gap Filling up to Max.: 5 mm Gap Width up to Max.: 25 mm Shelf Life (+5°C to +25°C / +41°F to +77°F): 12 months Shore A Hardness (DIN 5355 / ASTM D 224) ± 5: 42 Elongation at Break (DIN 53504/ASTM D 2240) ± 5: 650 % Tensile Strength of Pure Adhesive & Sealant: 3,3 N/mm² Average Tensile Shear Strength (DIN EN 1465/ ASTM D 12): 2,1 N/mm² Tear Strength (DIN 53515/ASTM D 1002): 20 N/mm² Movement Capacity Max.: 15 % Overpaintable (liquid paint): only “wet in wet“, within 3 hrs. at the latest after material app Building Material Category (DIN 412): B2 Temperature resistance: -40 to +90 °C Accessory: Press Pack Dosing Tip Workmanship Processing tube Squeeze out by hand, close tube again immediately after use, opened tubes should be used up as quickly as possible.

Processing press pack Remove original closure. Regulate discharge by smooth turning of the cap from min. to max.

Press the lever and process the product. After having turned the cap into the “min.” position the valve closes automatically and the product flow is stopped.

Joining the parts to be bonded to ensure optimal wetting, the parts must be joined before the first skin has been formed on the adhesive (skin-overtime).